QA

Quick Answer: Can You Use Polyurethane On Polymer Clay

Depending on the resins included, some brands of polyurethane can be softened by the plasticizers in your polymer clay. Often, as in the case with Varathane, they won’t cure rock-hard, but it won’t be sticky either. Other varnishes can be sticky, though, so always test a new varnish with the clay you’re using.

What do you seal polymer clay with?

Wax is the best polymer clay sealer to use if you want to perfectly maintain the texture of your work. If you’ve sanded and buffed your bead, the wax will give a wonderfully warm sheen. If you don’t sand and buff, it will give a more matte finish.

Can you use Minwax polyurethane on polymer clay?

Tested Minwax Fast-Drying Polyurethane (Oil Based) on a baked Premo Polymer Clay Bead. Sample was dipped and left to rest for 4 months. Finish has water-like consistency. Finish is hard, thin, smooth, semi-gloss, durable, not sticky and is compatible with polymer clay.

What do you coat polymer clay?

Matte varnish will give your polymer clay pieces a natural looking finish. It’s a little less glossy than wax, sealing in your work with a thin layer while retaining the overall look of the piece.

Can you seal polymer clay with Polycrylic?

You can apply a finish to polymer clay to give it a glassy shine without all that sanding and buffing. For general purposes, most polymer clay artists and hobbyists of the day are using water-based polyurethane finishes (such as Rust-Oleum’s Varathane or Minwax’s Polycrylic) or Future floor finish.

Should you paint polymer clay before or after baking?

Polymer clay doesn’t shrink or expand as it cures, meaning you can paint it before you bake. Unbaked clay may create a better bond with paint as it cures. Test different types and brands of paint to find the best results.

Do I need to seal acrylic paint on polymer clay?

Polymer clay’s natural qualities make it perfect for sculpting this style of sculpture. No varnish or sealer is needed, just a strong brand of clay (such as Premo) and your imagination.

Which is better Polycrylic or polyurethane?

The formula has an acrylic base; polyurethane is added for better adhesion and durability. Polycrylic is not as durable as polyurethane and is meant to be used only on interior surfaces such as cabinets, furniture, and trim.

What is the difference between Varathane and polyurethane?

The key difference between polyurethane urethane and varathane is that polyurethane is a polymer material and urethane is the linkage between the monomers of the polyurethane polymer, whereas varathane is a type of wood stain.

Does polymer clay break easily?

Polymer clay beads should be bendable if they are baked correctly. Under-baked polymer clay won’t be bendable. It will be brittle and easy to break.

Can I use clear nail polish on polymer clay?

It seems like such a simple solution to use nail polish to accent your polymer clay creations. Or use clear nail polish as a glaze. Don’t do it. The solvent in nail polish will begin to soften and dissolve your polymer clay, even baked clay, making it sticky and gooey over time.

How long should you cook polymer clay?

To bake polymer clay, preheat your oven to the manufacturer’s advised temperature (usually 230°F – 275°F). Baking times are typically 15 – 30 minutes for each ¼ inch thickness. Thinner clay needs 15 minutes to cure. When cool, properly baked clay can be marked with a fingernail, but it won’t sink in.

What paint do you use on polymer clay?

Craft Paints (and the supplies that go with it) are a must have for most polymer clay artists. I prefer acrylic paints and in many cases “heavy body” acrylic paints, but any type of acrylic craft paint is safe to use directly on polymer clay. You can use acrylic paints before baking OR after baking your clay.

How do you seal polymer clay with resin?

Simply place your polymer clay bead on a surface with raised bumps of some kind (preferably silicon). The resin will drip off the bead and pool in the grooves between the bumps, curing in its own puddle away from your project. Once cured simply pick your bead up off of the curing surface.

What’s the best glaze for polymer clay?

These polymer clay sealers and varnishes performed well on Sculpey III. PYM II. Sculpey Satin Glaze. Polycrylic Clear (satin and gloss) Varathane (satin and gloss) Final Coat (both semi-gloss and low-gloss) Cernit Matte Varnish. Swellegant Sealant. DuraClear Ultra Matte Varnish.

How do you make polymer clay shiny?

Polymer clay is not glossy after baking. You can sand, buff, and polish the clay itself (see below), or you can apply a glossy varnish. To make your clay project less shiny, you could apply a matte varnish. Note that adding a glossy varnish can make translucent polymer clay seem more clear.

How do you seal polymer clay after painting?

You can use a Wax, Acrylic Sealer, Varnish or Liquid Epoxy. If you want a smooth finish, then use sandpaper and wax to seal your Polymer Clay and if you painted your clay, then you should seal it with an Acrylic Sealer or Varnish.

Can you sand polymer clay after baking?

Sandpaper is used to sand your clay after it has been baked, however you must make sure that you are using Wet/Dry Sandpaper so that you can keep the polymer dust out of the air and use it with water. Start out with the more COARSE grits of sandpaper and than use a very FINE grit of sandpaper.

How do you connect two pieces of polymer clay?

To bond uncured polymer clay to another piece, it’s best to use liquid clay or other bakeable glue such as Kato Poly Paste or Sculpey Bake and Bond. To bond two pieces of cured polymer clay that will not be baked again, use a flexible superglue such as Loctite Gel Control, Zap-a-Gap, or Gorilla Glue GEL Superglue.

Can you use water with polymer clay?

you can use water. Cut up, crumble or break down the hardened polymer clay into small pieces. Then start kneading the clay. As it softens, you can take clay out, fold over and over.

Can you wet polymer clay?

As polymer clay is a waterproof oil based material it can get wet, either in it’s baked or unbaked state. Water can however make the clay a little more brittle, if a design is submerged after baking.